批发沙伯基础无卤阻燃耐老化PPE/PS NORYL LTA1350

Specific Gravity 1.11 g/cc1.11 g/ccASTM D792
Density 1.11 g/cc0.0401 lb/in³ISO 1183
Moisture Absorption 0.0600 %0.0600 %23°C / 50% RH; ISO 62
Water Absorption at Saturation 0.20 %0.20 %ISO 62
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
0.0050 - 0.0070 in/in
@Thickness 0.126 in
SABIC Method
Melt Flow 10 g/10 min
@Load 5.00 kg,
Temperature 280 °C
10 g/10 min
@Load 11.0 lb,
Temperature 536 °F
ASTM D1238
Melt Index of Compound 10 g/10 min
@Load 5.00 kg,
Temperature 280 °C
10 g/10 min
@Load 11.0 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Tensile Strength at Break 60.0 MPa8700 psiType I, 50 mm/min; ASTM D638

80.0 MPa11600 psi50 mm/min; ISO 527
Tensile Strength, Yield 80.0 MPa11600 psiType I, 50 mm/min; ASTM D638

83.0 MPa12000 psi50 mm/min; ISO 527
Elongation at Break 6.0 %6.0 %50 mm/min; ISO 527

18 %18 %Type I, 50 mm/min; ASTM D638
Elongation at Yield 4.8 %4.8 %Type I, 50 mm/min; ASTM D638

5.0 %5.0 %50 mm/min; ISO 527
Tensile Modulus 2.84 GPa412 ksi1 mm/min; ISO 527

2.85 GPa413 ksi5 mm/min; ASTM D638
Flexural Yield Strength 118 MPa17100 psi1.3 mm/min, 50 mm span; ASTM D790

131 MPa19000 psi2 mm/min; ISO 178
Flexural Modulus 2.77 GPa402 ksi1.3 mm/min, 50 mm span; ASTM D790

2.91 GPa422 ksi2 mm/min; ISO 178
Izod Impact, Notched 0.900 J/cm1.69 ft-lb/inASTM D256
 0.380 J/cm
@Temperature -30.0 °C
0.712 ft-lb/in
@Temperature -22.0 °F
ASTM D256
Izod Impact, Unnotched 14.0 J/cm26.2 ft-lb/inASTM D4812
Izod Impact, Notched (ISO) 4.00 kJ/m²1.90 ft-lb/in²80*10*4; ISO 180/1A
 3.00 kJ/m²
@Temperature -30.0 °C
1.43 ft-lb/in²
@Temperature -22.0 °F
80*10*4; ISO 180/1A
Izod Impact, Unnotched (ISO) 35.0 kJ/m²16.7 ft-lb/in²80*10*4; ISO 180/1U
 34.0 kJ/m²
@Temperature -30.0 °C
16.2 ft-lb/in²
@Temperature -22.0 °F
80*10*4; ISO 180/1U
Charpy Impact, Notched 0.300 J/cm²1.43 ft-lb/in²Edgew 80*10*4 sp=62mm; ISO 179/1eA
Dart Drop, Total Energy 17.0 J
@Temperature 23.0 °C
12.5 ft-lb
@Temperature 73.4 °F
ASTM D3763

PPO性能

   1、PPO综合性能良好,可在120度蒸汽中使用,电绝缘性好,吸水小,但有应力开裂倾向。改性聚苯醚可消除应力开裂。

  2、有突出的电绝缘性和耐水性优异,有较好的耐磨性和电性能,尺寸稳定性好。其介电性能居塑料的首位。

  3、MPPO为PPO与HIPS共混制得的改性材料,市面上的材料均为此种材料。

  4、PPO有较高的耐热性,玻璃化温度211度,熔点268度,加热至330度有分解倾向,PPO的含量越高其耐热性越好,热变形温度可达190度。

  5、PPO阻燃性良好,具有自息性,与HIPS混合后具有中等可燃性。质轻,***可用于食品和***行业。耐光性差,长时间在阳光下使用会变色。



批发沙伯基础无卤阻燃耐老化PPE/PS NORYL LTA1350

以上为"批发沙伯基础无卤阻燃耐老化PPE/PS NORYL LTA1350"供应信息
相关推荐
产品分类 更多 >
新品速递 查看更多 >
中国供应商> 工程塑料> PPO> 批发沙伯基础无卤阻燃耐老化PPE/PS NORYL LTA1350
留言 进店 QQ交谈 电话联系
获取最低报价
提交留言