代理沙伯基础20%GF增强PPE/PS NORYL IGN320汽车点火线圈

Density / Specific Gravity

1.20

g/cm³

ASTM D792

Melt Mass-Flow Rate (MFR) (300°C/5.0 kg)

13

g/10 min

ASTM D1238

Molding Shrinkage



Internal Method

Across Flow : 3.20 mm

0.20 to 0.40

%


Flow : 3.20 mm

0.10 to 0.30

%


Mechanical

Nominal Value

Unit

Test Method

Tensile Modulus 1

6260

MPa

ASTM D638

Tensile Strength 2



ASTM D638

Yield

108

MPa


Break

108

MPa


Tensile Elongation 2 (Break)

2.4

%

ASTM D638

Flexural Modulus 3 (50.0 mm Span)

5720

MPa

ASTM D790

Flexural Strength 3 (Break, 50.0 mm Span)

170

MPa

ASTM D790
Impact

Nominal Value

Unit

Test Method

Notched Izod Impact (23°C)

100

J/m

ASTM D256

Unnotched Izod Impact (23°C)

510

J/m

ASTM D4812

Instrumented Dart Impact (23°C, Total Energy)

16.0

J

ASTM D3763
Thermal

Nominal Value

Unit

Test Method

Deflection Temperature Under Load



ASTM D648

0.45 MPa, Unannealed, 3.20 mm

164

°C


1.8 MPa, Unannealed, 3.20 mm

158

°C


Vicat Softening Temperature

175

°C

ASTM D1525 4
Electrical

Nominal Value

Unit

Test Method

Dielectric Strength (1.60 mm, in Oil)

34

kV/mm

ASTM D149

   PPO材料作为世界五大通用工程塑料之一,***,相对密度小,(PPO/PA同类产品也仅为1.10-1.13g/cm3),是五大通用工程塑料中密度最小的,具有良好的机械强度,抗蠕变性,耐应力松弛,抗疲劳强度高。


     PPO/PS合金耐热性突出,热变形温度在1.82MPa下,可以从75-170℃连续变化,随着PPO含量增加,材料的热变汽车工业形温度不断升高,用于满足不同场合的性能需求。PPO及其合金可以采用注塑、挤出、模压、发泡和电镀、真空镀膜、印刷机加工等各种加工方法。



代理沙伯基础20%GF增强PPE/PS NORYL IGN320汽车点火线圈

以上为"代理沙伯基础20%GF增强PPE/PS NORYL IGN320汽车点火线圈"供应信息
相关推荐
产品分类 更多 >
新品速递 查看更多 >
中国供应商> 工程塑料> PPO> 代理沙伯基础20%GF增强PPE/PS NORYL IGN320汽车点火线圈
留言 进店 QQ交谈 电话联系
获取最低报价
提交留言