PC/日本三菱产品的应用

 

 

PC plastic raw materials known as polycarbonate, polycarbonate English name for the Polycarbonate, referred to as PC, is non crystalline thermoplastics. It is a general term for polymer compound carbonate structure containing a class of molecular chain and various materials and prepared based on it. According to the molecular structure of the ester can be divided into different aliphatic, cycloaliphatic, aromatic and aliphatic and aromatic and other categories. And with bisphenol A polycarbonate is the most important, the molecular weight is generally 3 - 100000. In the absence of special circumstances, usually said the polycarbonate of bisphenol A polycarbonate and its modified varieties. Due to their excellent mechanical properties, commonly known as bulletproof glue

 

  

PC是一种非晶体工程材料,具有特别好的抗冲击强度、热稳定性、光泽度、抑制细菌特性、阻燃特性以及抗污染性。PC的缺口伊估德冲击强度(otched Izod impact stregth)非常高,并且收缩率很低,一般为0.1%~0.2%。

 

光学照明:用于制造大型灯罩、防护玻璃、光学仪器的左右目镜筒等,还可广泛用于飞机上的透明材料。

 

电子电器:聚碳酸酯是优良的E(120℃)级绝缘材料,用于制造绝缘接插件、线圈框架、管座、绝缘套管、电话机壳体及零件、矿灯的电池壳等。也可用于制作尺寸精度很高的零件,如光盘、电话、电子计算机、视频录象机、电话交换器、信号继电器等通讯器材。聚碳酸酯薄摸还被广泛用作电容器、绝缘皮包、录音带、彩色录象磁带等。

 

机械设备:用于制造各种齿轮、齿条、蜗轮、蜗杆、轴承、凸轮、螺栓、杠杆、曲轴、棘轮,也可作一些机械部件护罩、罩盖和框架等零件。

 

医疗器材:可作医疗用途的杯、筒、瓶以及牙科器械、药品容器和手术器械,甚至还可用作人工肾、人工肺等人工脏器。

 

其它方面:建筑上用作中空筋双壁板、暖房玻璃等;在纺织行业用作纺织纱管、纺织机轴瓦等;日用方面作奶瓶、餐具、玩具和模型等

 

 

PC/日本三菱产品性能

 

 

1, with high strength and elastic modulus, high impact strength, wide range of usage temperature.

2、高度透明性及自由染色性。

2,a high degree of transparencyand free dyeing.

3、H.D.T.高。

3, H.D.T. high.

4、电气特性优。

4, the electrical characteristics.

5、无味无臭对人体无害符合卫生安全。6、成形收缩率低、尺寸安定性良好 。

5, odorless harmless to the human body to meet health and safety. 6, forming low shrinkage, good dimensional stability.

电子电器:CD片、开关、家电外壳、信号筒、电话机。

Electronics: CD, switch, electrical appliance shell, barrel, telephone signal.

汽 车: 保险杆、分电盘、安全玻璃。

Car: bumper, distributor, safety glass.

工业零件:照相机本体、机具外壳、安全帽、潜水镜、安全镜片。

Industrial parts: a camera body, machine shell, helmets, goggles, safety glasses.

耐热,抗冲击,阻燃,在普通使用温度内都有良好的机械性能。同性能接近聚甲基相比,聚碳酸酯的耐冲击性能好,折射率高,加工性 能好,不需要添加剂就具有UL94 V-0级阻燃性能。但是聚甲基相对聚碳酸酯价格较低,并可通过本体聚合的方法生产大型的器件。随着聚碳酸酯生产规模的日益扩大,聚碳酸酯同聚甲 基之间的价格差异在日益缩小。聚碳酸酯的耐磨性差。一些用于易磨损用途的聚碳酸酯器件需要对表面进行特殊处理

Heat resistant, impact resistant, flame retardant, have good mechanical properties in common use temperature range. Isotropic to polymethylmethacrylate, polycarbonate good impact resistance, high refractive index, processing is good, need not additive with UL94 class V-0 flame retardant properties. But the relatively low price of PMMA polycarbonate, method and through polymerization production of large devices. With the growing scale of production of polycarbonate, polycarbonate with between poly methyl methacrylate price difference in the increasingly narrow. Wear resistance of polycarbonate difference. For easy to wear some polycarbonate devices use requires special treatment on the surface








物理性能

额定值

单位制

测试方法

密度

1.20

g/cm³

ISO 1183

溶化体积流率(MVR) (300°C/1.2 kg)

2.30

cm³/10min

ISO 1133

收缩率



ISO 294-4

垂直流动方向

0.60

%


流动方向

0.60

%


机械性能

额定值

单位制

测试方法

拉伸模量

2300

MPa

ISO 527-2

拉伸应力 (屈服)

62.0

MPa

ISO 527-2

拉伸应变 (屈服)

6.0

%

ISO 527-2

标称拉伸断裂应变

> 50

%

ISO 527-2

弯曲模量

2300

MPa

ISO 178

弯曲应力

93.0

MPa

ISO 178
冲击性能

额定值

单位制

测试方法

简支梁缺口冲击强度 (23°C)

70

kJ/m²

ISO 179/1eA

简支梁无缺口冲击强度 (23°C)

无断裂


ISO 179/1eU

热性能

额定值

单位制

测试方法

热变形温度 (1.8 MPa, 未退火)

129

°C

ISO 75-2/A

线形热膨胀系数



ISO 11359-2

流动

6.5E-5

cm/cm/°C


横向

6.6E-5

cm/cm/°C









霆尔代理进口原料Iupilon® PC日本三菱工程RS-1001R

霆尔代理进口原料Iupilon® PC日本三菱工程EB-3001R

霆尔代理进口原料Iupilon® PC日本三菱工程LCH2315

霆尔代理进口原料Iupilon® PC日本三菱工程LCH2410

霆尔代理进口原料Iupilon® PC日本三菱工程LCH2415

霆尔代理进口原料Iupilon® PC日本三菱工程LGH2230M

霆尔代理进口原料Iupilon® PC日本三菱工程LGH2330M

霆尔代理进口原料Iupilon® PC日本三菱工程M7020AD2

PC塑料如果你还是觉得陌生的话,那么再举一个例子,这就是咱们小时候玩的四驱车车壳、底盘等等,都是PC塑料,这种材质在玩具、模型界被广泛的运用,主要是因为改造型较强,用硝基稀料就能够充当“胶水”来粘合,但就是这种常用的材质,也是有硬伤的。PC材质在很多领域都表现甚好,在手机壳领域中更是有着比较全面的体现,众多厂商都上市了一些PC塑料材质的手机壳,主要是因为造假比较便宜,制作工艺要求的也不高,有些PC塑料质地比较软,绝缘性还是可以的;TPU材质也是如此,类似硅胶的性质对于电流有着相对较好的绝缘,而PP材质却不是很如意。

pc塑料壳指的是聚碳酸酯(PC)是碳酸的聚酯类,碳酸本身并不稳定,但其衍生物(如光气,尿素,碳酸盐,碳酸酯)都一定稳定性。按醇结构的不同,可将聚碳酸酯分成脂族和芳族两类。脂族聚碳酸酯。如聚亚乙基碳酸酯,聚三亚甲基碳酸酯及其共聚物,熔点和玻璃化温度低,强度差,不能用作结构材料;但利用其生物相容性和生物可降解的特性,可在药物缓释放载体,手术缝合线,骨骼支撑材料等方面获得应用。聚碳酸酯耐弱酸,耐弱碱,耐中性油。聚碳酸酯不耐紫外光,不耐强碱。PC是一种线型碳酸聚酯,分子中碳酸基团与另一些基团交替排列,这些基团可以是芳香族,可以是脂肪族,也可两者皆有。双酚A型PC是***重要的工业产品。PC是几乎无色的玻璃态的无定形聚合物,有很好的光学性。PC高分子量树脂有很高的韧性,悬臂梁缺口冲击强度为600~900J/m,未填充牌号的热变形温度大约为130°C   ,玻璃纤维增强后可使这个数值增加10°C。PC的弯曲模量可达2400MPa以上,树脂可加工制成大的刚性制品。低于100°C   时,在负载下的蠕变率很低。PC耐水解性差,不能用于重复经受高压蒸汽的制品。