韩国乐天阻燃高流动ABS Starex NH-0826
Density / Specific Gravity(Natural) | 1.05 | g/cm | ASTM D792,ISO 1183 |
Melt Mass-Flow Rate (MFR) | |||
200°C/5.0 kg | 6.0 | g/10 min | ASTM D1238 |
220°C/10.0 kg | 65 | g/10 min | ISO 1133 |
Molding Shrinkage | |||
Flow : 3.20 mm | 0.30 to 0.60 | % | ASTM D955 |
Across Flow : 3.20 mm | 0.30 to 0.60 | % | ASTM D955 |
Across Flow : 2.00 mm | 0.30 to 0.60 | % | ISO 294-4 |
Flow : 2.00 mm | 0.30 to 0.60 | % | ISO 294-4 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness | |||
R-Scale | 111 | ASTM D785 | |
R-Scale | 113 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
--2 | 2100 | MPa | ASTM D638 |
-- | 2400 | MPa | ISO 527-2/50 |
Tensile Strength | |||
Yield2 | 42.0 | MPa | ASTM D638 |
Yield | 48.0 | MPa | ISO 527-2/50 |
Break2 | 39.0 | MPa | ASTM D638 |
Break | 34.0 | MPa | ISO 527-2/50 |
Flexural Modulus | |||
--3 | 2300 | MPa | ASTM D790 |
--4 | 2400 | MPa | ISO 178 |
Flexural Strength | |||
--3 | 64.0 | MPa | ASTM D790 |
--4 | 76.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength5(23°C) | 18 | kJ/m | ISO 179/1eA |
Notched Izod Impact | |||
23°C, 3.18 mm | 150 | J/m | ASTM D256 |
23°C, 6.35 mm | 140 | J/m | ASTM D256 |
23°C5 | 15 | kJ/m | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
1.8 MPa, Unannealed, 6.40 mm | 82.0 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm | 75.0 | °C | ISO 75-2/A |
Vicat Softening Temperature | 94.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
Flame Rating | UL 94 | ||
0.75 mm | V-2 | ||
3.0 mm | V-2 |
ABS物料性能
1.综合性能较好,冲击强度较高,化学稳定性,电性能良好；
2.与372有机玻璃的熔接性良好,制成双色塑件,且可表面镀铬,喷漆处理；
3.有高抗冲、高耐热、阻燃、增强、透明等级别；
4.流动性比HIPS差一点，比PMMA、PC等好，柔韧性好；
5.适于制作一般机械零件,减磨***零件,传动零件和电讯零件。